The fabrication of vanadium oxide films directly on Si(100) substrates by plasma atomic layer deposition(ALD) with vanadium oxytriisopropoxide(VOIP) and oxygen as the reactants have been performed at temperature ranging from 250 to $450^{circ}C$. Growth rate of vanadium oxide was $2.8{AA}$/cycle at $300{sim}400^{circ}C$ defined as ALD acceptable temperature window, Vanadium oxide has been shown the different phases at $250^{circ}C$ and more than $300^{circ}C$. It has been confirmed that the phase of the films deposited at $250^{circ}C;was;V_2O_5$ type and that of the films above $300^{circ}C;was;VO_2(T)$ type measured at room temperature, respectively. A large change in resistance and small temperature hysteresis corresponding to a temperature has been observed in the vanadium oxide film deposited at temperature $350^{circ}C$.