The SiOC film of carbon centered system was prepared using bistrimethylsilylmethane and oxygen mixed precursor by the chemical vapor deposition. The chemical properties of the SiOC film were analyzed by the I-V measurement and FTIR spectra analysis. The main bond of $950{sim}1200cm^{-1}$ was composed of the Si-C, Si-O-C and Si-O bonds. The leakage current of the SiOC film increased with the increasing of the carbon content, and the drift of the current was in proportion to the Si-O-C bond content. The deconvoluted data of FTIR spectra could be classified the three types such as organic, hybrid and inorganic types, and the contact angle showed the difference of three types.