In this study, $(K_{0.5}Na_{0.5})(Nb_{0.97}Sb_{0.03})O_3+0.9$ mol% $K_{5.4}Cu_{1.3}Ta_{10}O_{29}+x$ mol% $K_4CuNb_8O_{23}$ (x = 0, 0.2, 0.6, 0.8) ceramics were prepared by a conventional mixed oxide method. Their microstructure and electric properties were investigated. The secondary phase was made by virtue of $K_4CuNb_8O_{23}$ (KCN) addition in the $(K_{0.5}Na_{0.5})(Nb_{0.97}Sb_{0.03})O_3$ system ceramics. However, the sinterability of the ceramics increased with increasing $K_4CuNb_8O_{23}$ content. At the 0.6 mol% $K_4CuNb_8O_{23}$ added composition ceramics sintered at $1,060^{circ}C$, kp and $d_{33}$ showed the optimum values of 0.39 and 145 pC/N, respectively, suitable for piezoelectric actuator application.