New poly(arylene ether)s (PAEs) with both transparency and heat-resistance were prepared by a polycondensation of FBPODS, an ordered-sequence aromatic dihalide, and cardo typed aromatic diols containing fluorene and/or adamantane moiety and also non-cardo typed 1,5-naphthalene diol. The resulting polymers had their glass transition temperatures ranged from 202 to $247^{circ}C$. Based on TGA data, they exhibited excellent thermal stabilities, showing 5% weight loss at $434-487^{circ}C$. They had low thermal expansion coefficients of 58-59 ppm at temperature range of $50-200^{circ}C$ as well as good mechanical properties with moduli of 1757-2143 MPa. The optical transmittance for the PAE films was over 70% at 550 nm, except for the PAE that contains naphthalene moiety (30% at 550 nm). They also showed water uptake of about 0.68% regardless of their chemical compositions. Therefore, the newly developed PAEs show strong potential as plastic substrates for flexible devices for display, solar cell and e-paper.