This study examines the photoelectric conversion efficiency of dye-sensitized solar cells (DSSCs) when nanometer-sized Zr (0.1, 0.5, and 1.0 mol %)-$TiO_2$ prepared using a solvothermal method is utilized as the working electrode material. The particle sizes observe in the transmission electron microscopy (TEM) images are < 30 nm in all samples. The absorption band is slightly broadened at the tail for the 0.1 mol % Zr-$TiO_2$, and the intensity of the photoluminescence (PL) curves of the Zr-incorporated $TiO_2$ is significantly smaller than that of the pure $TiO_2$. Compared to that using pure $TiO_2$, the energy conversion efficiency is enhanced considerably by the application of Zr-$TiO_2$ in the DSSCs to approximately 6.17% for 0.5 mol % Zr-$TiO_2$ with the N719 dye (10.0 ${mu}m$ film thickness and 5.0 mm ${ imes}$ 5.0 mm cell area) under 100 mW/$cm^2$ of simulated sunlight.