Emerald (3BeO{cdot}Al$_{2}$O_{3}{cdot}6SiO_2 : Cr^{3+}$</TEX>) single crystals were grown by flux method of $Li_2O-MoO_3 - V_2O_5$ system. The composition of starting materials were 1, 3, 5 mole ratio of $MoO_3 - V_2O_5/$Li_2O$, 20 - 15% of emerald content to flux composition and 1% of $Cr_2O_3$ colordopant to emerald composition. After mixing those were melted at $1100^{circ}C$ in Pt crucible of electric furnace. Single crystal growth was cooled down slowly rate of $3^{circ}C$/hr from $1100^{circ}C$ to $650^{circ}C$, for the cooling period it was controlled and prevented the nucleation of microcrystallite from variation of each thermal fluctuation range. Specially it has been obtained plenty of large emerald single crystal when thermal fluctuation was treated for cooling period at $1050 ~ 950^{circ}C$, in 3 mole ratio of $V_2O_5 - MoO_3/Li_2O$ flux. Emerald single crystal growing effect and $Cr_{+3}$ ion of substitutional solid solution effect for $Al_{+3}$ ion was good than mole ratio of 5. Emerald single crystals were c (0001) hexagonal rystal face of preferencial direction and m (1010) post side. Emerald was hexagonal columnar greenish transparent and 2.65 ~ 2.66 of specific gravity.