We have grown undoped $In_ xGa_{1-x}N,; In_xGa_{1-x}N:Si;and;In_{0.1}Ga_{0.9}N:Zn$ thin films by MOCVD at temperature between 880 and $710^{circ}C which endows various In composition in the epilayer from 0.07 to 0.22 as examined using X-ray diffraction, optical absorption(OA), photocurrent (PC) and photoluminescence (PL). The In molar fraction estimated from PL results is higher than that from the OA, PC, and X-ray data for $X{le}0.22$, which may be caused by phase separation. However, the In molar fraction estimated by X-ray diffraction, OA, PC and PL for $In_xGa_{1-x}N:Si$ does not show discrepancy. With the appropriate Zn doping in undoped $In_{0.1}Ga_{0.9}N$, the emission peak is shifted from 3.15 eV which originates from the band edge emission peak to 2.65 eV which resulted from the conduction band to acceptor transition due to a deep acceptor level.