New organic light-emitting diodes with structure of ITO/DNTPD/TAPC/$Bebq_2/Bebq_2$:RP-411/ET-137/LiF/Al using the selective doping of 5% RP-411 in a single $Bebq_2$ host in the two wavelength(green, red) emitter formation were proposed and characterized. In the experiments, with a 300${AA}$-thick undoped emitter of $Bebq_2$, three kinds of devices with different thicknesses of 30${AA}$, 40${AA}$ and 50${AA}$ in the doped emitter of $Bebq_2$:RP-411 were fabricated. The electroluminescent spectra showed two peak emissions at the same wavelengths of 511 nm and 622 nm for the fabricated devices. When the device with a 30${AA}$-thick doped emitter is referred as "D-1", the device with a 40${AA}$-thick doped emitter is referred as "D-2" and the device with a 50${AA}$-thick doped emitter is referred as "D-3", the relative intensity of 622 nm to 511 nm at two wavelength peaks was higher in the D-2 and the D-3 than in the D-1. The devices of D-1, D-2 and D-3 showed the color coordinates of (0.43, 0.46), (0.46, 0.44) and (0.48, 0.43) on the CIE chart, respectively.